SilverTip Laminating Epoxy Resin

Product Description

SilverTip Epoxy is a medium-low viscosity, liquid epoxy resin system that has been optimized for coating and reinforcing fabric saturation in wood-composite boat building. It will outperform any other product in these applications. SilverTip Epoxy is designed for use with fiberglass, Kevlar®, Dynel® and graphite as well as on bare wood. It has superior wet-out characteristics with little tendency to foam or trap air.

Both the resin and hardener are nearly colorless and are used in an easy 2:1 volumetric ratio. SilverTip Epoxy cures to a brilliant blush-free film with either the fast or slow hardener eliminating secondary bonding concerns as experienced with other epoxies. The working time is longer than most boat building epoxies without extending cure time. The cured film is tough and resilient with better heat resistance than other epoxies cured at room temperature. Fillers, wood flour, and bulking agents can be combined with SilverTip Epoxy, however, we suggest using the other members of the SilverTip series for adhesive, filleting and fairing applications.

  • Exceptionally fast wet-out of fiberglass and other reinforcing media.
  • Superior defoaming properties and little tendency to float fabric.
  • Resistance to print-through.
  • Has excellent hot weather performance following a mild post-cure compared to most room 
  • temperature cure resin systems.
  • Cures without forming an amine blush with either the fast or slow hardener.
  • Cures quickly to a sandable state (no sanding required between coats when recoating within 72 hours). 
  • Sandable same day with fast hardener.
  • Features a convenient 2:1 mixing ratio.
  • Use either a slow or fast hardener or blend the two hardeners for even more flexibility in working time.
  • Cures exceptionally clear for bright finished applications.
  • Compatible with all 2-part and most 1-part marine primers.
  • SilverTip Slow Hardener can be post-cured for even greater high temperature resistance and elevated mechanical specifications.
Size
$ 38.30
Mix Ratio by Volume 100:50
Mix Ratio by Weight 100:43
Total Solids 100%
Mixed Viscosity 700 cps
Mixed Color Colorless to Light Yellow
Coverage See Appendix A
Maximum Service Temperature 160°F (70°C)
Tensile Strength, psi 7,900
Tensile Elongation 8%
Flexural Strength, psi 13,000
Flexural Modulus, psi 420,000
Compressive Strength, psi at yield: 13,000
  at failure: 26,000
Gel Time @ 77°F (25°C) Fast Hardener: 26 Minutes (100g mixture)
  Slow Hardener: 60 Minutes (100g mixture)
Tack Free Time Thin Film@ 77°F (25°C) Fast Hardener: 3 Hours
  Slow Hardener: 6 Hours
Minimum Application Temperature Fast Hardener: 35°F (2°C)
  Slow Hardener: 55°F (13°C)