Clear Coat

Product Description

Clear Coat is an extremely low viscosity, water white, "penetrating" epoxy system. Clear Coat cures to a brilliantly clear, very tough finish without the usual "amine blush" associated with some epoxy resin films. Clear Coat contains no volatile solvents.

Turbo Cure may be added speed up cures during cold weather. Use a maximum of 1 fluid ounce per quart of resin. A two part epoxy coating and laminating resin for use in marine and woodworking applications. Use as a sealer, topcoat, saturation coat or tie-coat.

  • Features a convenient 2:1 mixing ratio.
  • A clear, almost water-white, solvent-free epoxy system. 
  • Cures to a clear, glossy, blush-free surface.
Size
$ 41.40
Mix Ratio by Volume 100:50
Mix Ratio by Weight 100:43
Total Solids 100%
Mixed Viscosity 400 cps
Minimum Application Temperature 60°F (16°C)
Tensile Strength, psi 7,800
Tensile Elongation at Break 8%
Flexural Strength, psi 12,000
Flexural Modulus, psi 375,000
Compressive Strength, psi Yield 13,000
Failure 26,000
Coverage  See Appendix A
Minimum Application Temperature 50°F (10°C)
Minimum Application Temperature with 2% Turbo Cure 45°F (7°C)
Gel Time @ 77°F (25°C) 60 Minutes (100g mixture)
Gel Time @ 77°F (25°C) with 2% Turbo Cure 30 Minutes (100g mixture)
Tack FreeTime Thin Film @ 77°F (25°C) 48 Hours
Full Cure @ 77°F (25°C) 72 Hours

Clear Coat is ideal for clear coating wood, and the wetting out of fiberglass cloth for bright finished boats. Use as a build coat for clear linear polyurethane or varnish coatings and as a penetrating first coat for blister repair on fiberglass boats. Use also for those applications that require a long pot life and low viscosity. Use Clear Coat as the sole epoxy system to make wood strip canoes and kayaks. Protect Clear Coat from moisture during cure to avoid water spotting.